AKROLOY®
PA GF 50 8 black (6732)PA66+PA6I/6T GF50
AKROLOY® PA GF 50 8 black (6732) is a 50% glass fiber reinforced, semi-aromatic polyamide blend. It is characterised by lower moisture absorption compared to standard PA 6.6 compounds, thus convincing through very high stiffness and strength even in the conditioned state. The material is therefore perfectly suitable for technical applications with high demands for dimensional stability. Furthermore, it can be used as an alternative for aluminium and zinc diecast alloys. The compound fulfill FDA, EU10/2011 and ACS.
Features
Regulatory
Properties
17.500MPa
260MPa
105kJ/m²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Flexural strength
ISO 178
Flexural strain at break
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Temperature of deflection under load HDT/C
ISO 75
Melting temperature
ISO 11357-3
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Molding shrinkage
ISO 294-4
Documents
Discover all the technical specifications at a single glance here.
Processing information
The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problem and surface defects.
Drying time
0 - 4 h
Drying temperature (τ ≤ -30°C)
80 °C
Processing moisture
0,02 - 0,1 %
Feed section
60 - 80 °C
Temperature Zone 1 - Zone 4
260 - 300 °C
Nozzle temperature
270 - 300 °C
Melt temperature
280 - 300 °C
Mold temperature
90 - 130 °C
Holding pressure, spec.
300 - 800 bar
Back pressure, spec.
50 - 150 bar
Injection speed
medium to high
Screw speed
8 - 15 m/min
Applications
Explore more exciting application examples that illustrate how our products can be beneficial to you in various situations and industries.
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.