Preliminary datasheet

PK – Polyketone PK

AKROTEK® PK-VM 8 black (6466)

1700 MPa

n.b. kJ/m²

AKROTEK® PK-VM 8 black (6466) is an unreinforced, low viscous polyketone. The material fulfills the requirements according to the KTW guidline for cold and hot water and the DVGW worksheet W 270.

Typical applications

Mainly components in domestic and industrial applications that are in contact with food or drinking water.

Regulatory

KTW_cold_KTW_hot_W270

Processing information

The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.

6Drying time0 - 4 h
Drying temperature80°C
Processing moisture0,02 - 0,1%
1Feed section60 - 80°C
2Temperature zone 1 - Zone 4220 - 250°C
3Nozzle temperature230 - 250°C
4Melting temperature230 - 250°C
5Mold temperature60 - 120°C
P NachHolding pressure, spec.300 - 800 bar
P StauBack pressure, spec.30 - 70 bar
Injection speedmedium to high
Screw speed8 - 15 m/min

Warning

The molding machine needs to be purged with polyolefines before and after processing of AKROTEK® PK! There is a risk of cross linking caused by reactions with POM or PA as well as unsuitable master batches! Cross linking is visible through dark spots! In this case purge immediately with polyolefines.

  • Mechanical Properties
    Tensile modulus (1 mm/min | ISO 527-2)
    d.a.m.1700 MPa
    conditioned1700 MPa
    Stress at yield (50 mm/min | ISO 527-2)
    d.a.m.60 MPa
    conditioned60 MPa
    Strain at break (50 mm/min | ISO 527-2)
    d.a.m.> 100 %
    conditioned>100 %
    Charpy impact strength (23°C | ISO 179-1/1eU)
    d.a.m.n.b. kJ/m²
    conditionedn.b. kJ/m²
    Charpy notched impact strength (23°C | ISO 179-1/1eA)
    d.a.m.12 kJ/m²
    conditioned12 kJ/m²
  • Thermal Properties
    Temperature of deflection under load HDT/A (1,8 MPa | ISO 75)100 °C
    Melting temperature (DSC, 10K/min | DIN EN 11357-1)220 °C
  • Flammability
    Burning rate UL 94 1,6mm Wall thickness (UL 94)HB Class
  • General properties
    Density (23°C | ISO 1183)1,24 g/cm³
    Humidity absorption (70°C, 62% r.F. | ISO 1110)0,8 - 0,9 %
    Molding shrinkage (flow | ISO 294-4)2,0 %
    Molding shrinkage (transverse | ISO 294-4)2,0 %
  • Electrical Properties
    Volume resistivity (IEC 60093)
    d.a.m.1,0E+13 Ohm x cm
    Surface resistivity (acc. to IEC 60093)
    d.a.m.1,0E+13 Ohm
  • Rheological Properties
    MVR (240°C/2,16kg | ISO 1133)50 cm³/10min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK® and ICX® are registered trademarks of the Feddersen Group.