PA6.6 – Polyamide 6.6 PA66 GF50
AKROMID® A28 GF 50 9 EN MCL black (6429)
AKROMID® A28 GF 50 9 EN MCL black (6429) is a 50% glass fibre reinforced, process improved, foam injection moulding improved, electrical neutral, easy flowing polyamide 6.6 with very high rigidity and strength.
Components in mechanical engineering and housings for electronic parts in the automotive industry. AKROMID® A28 GF 50 9 EN MCL black (6429) is suitable for structural foam moulding.
The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.
|Drying time||0 - 4 h|
|Drying temperature (τ ≤ -30°C)||80°C|
|Processing moisture||0,02 - 0,1%|
|Feed section||60 - 80°C|
|Temperature zone 1 - Zone 4||260 - 300°C|
|Nozzle temperature||270 - 310°C|
|Melt temperature||280 - 300°C|
|Mold temperature||80 - 100°C|
|Holding pressure, spec.||300 - 800 bar|
|Back pressure, spec.||50 - 150 bar|
|Injection speed||medium to high|
|Screw speed||8 - 15 m/min|
- Mechanical Properties
Tensile modulus (1 mm/min | ISO 527-2) d.a.m. 16700 MPa Stress at break (5 mm/min | ISO 527-2) d.a.m. 250 MPa Strain at break (5 mm/min | ISO 527-2) d.a.m. 2,5 % Flexural modulus (2 mm/min | ISO 178) d.a.m. 15200 MPa Flexural strength (2 mm/min | ISO 178) d.a.m. 380 MPa Charpy impact strength (23°C | ISO 179-1/1eU) d.a.m. 95 kJ/m² Charpy impact strength (-30°C | ISO 179-1/1eU) d.a.m. 95 kJ/m² Charpy notched impact strength (23°C | ISO 179-1/1eA) d.a.m. 17 kJ/m² Charpy notched impact strength (-30°C | ISO 179-1/1eA) d.a.m. 14 kJ/m² Ball indentation hardness (961N/30s | ISO 2039-1) d.a.m. 290 MPa
- Thermal Properties
Melt temperature (DSC, 10K/min | DIN EN 11357-1) 262 °C
Burning rate (UL 94) 0,8mm Wall thickness HB Class Burning rate (<100 mm/min) (> 1 mm Thickness | FMVSS 302) +
- General properties
Density (23°C | ISO 1183) 1,57 g/cm³
- Electrical Properties
Surface resistivity (acc. to IEC 60093) d.a.m. 1,0E+12 Ohm Dieletric strength (3 mm | IEC 60243) 600 kV/mm
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
You have questions about our products?
With a worldwide network of plastics distribution experts, we can provide you with support anywhere in the world. Talk to one of our specialists to find out more.CONTACT US NOW