PPA – Polyphthalamide PPA GF50
AKROMID® T5 GF 50 6 black (6331)
AKROMID® T5 GF 50 6 black (6331) is a 50% glass fibre reinforced, inorganic high heat stabilised polyphthalamide with very high stiffness and strength.
Parts with tight dimensional tolerances even under high mechanical load.
The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.
|Drying time||0 - 4 h|
|Processing moisture||0,02 - 0,1%|
|Feed section||60 - 90°C|
|Temperature zone 1 - Zone 4||320 - 350°C|
|Nozzle temperature||330 - 350°C|
|Melting temperature||330 - 350°C|
|Mold temperature||120 - 160°C|
|Holding pressure, spec.||300 - 800 bar|
|Back pressure, spec.||50 - 150 bar|
|Injection speed||medium to high|
|Screw speed||8 - 15 m/min|
- Mechanical Properties
Tensile modulus (1 mm/min | ISO 527-2) d.a.m. 18000 MPa Stress at break (5 mm/min | ISO 527-2) d.a.m. 275 MPa
- Thermal Properties
Temperature of deflection under load HDT/A (1,8 MPa | ISO 75) 280 °C Temperature of deflection under load HDT/C (8 MPa | ISO 75) 235 °C Melting temperature (DSC, 10K/min | DIN EN 11357-1) 325 °C
Burning rate UL 94 1,6mm Wall thickness (UL 94) HB Class
- General properties
Density (23°C | ISO 1183) 1,61 g/cm³
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK® and ICX® are registered trademarks of the Feddersen Group.
You have questions about our products?
With a worldwide network of plastics distribution experts, we can provide you with support anywhere in the world. Talk to one of our specialists to find out more.CONTACT US NOW