AKROMID®

D3 CGM 15/20 S1 black (6284)PA612 (CF15+GF20)

AKROMID® D3 CGM 15/20 S1 black (6284) is a 15% carbon fibre reinforced, 20% glass fibre reinforced, cold impact strength polyamide 6.12 with high stiffness and strength and electrical conductivity. Due to its good chemical resistance, the compound is suitable for media-carrying connectors and can replace PA12 in certain applications.

Properties

Modulus

13.500MPa

Strength

145MPa

Impact

80kJ/m²

Mechanical Properties


Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
13500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
145 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
4 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
13000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
235 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
30°C | d.a.m.
-
80 kJ/m²
80 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
25 kJ/m²

Thermal Properties


Melting temperature

ISO 11357-3

DSC, 10K/min
215 °C

Flammability


Burning rate

UL 94

0,8 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties


Density

ISO 1183

23°C
1,23 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,3 - 0,5 %
0,8 - 1,0 %

Electrical Properties


Volume resistivity IEC

DIN EN 62631-3-2

d.a.m.
< 106 Ω x cm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.