AKROMID® B3 GF 30 1 L black (5661)

AKROMID® B3 GF 30 1 L black (5661) is a 30% glass fibre reinforced and heat stabilised polyamide-blend with a reduced density compared to standard PA6 GF 30

Typical applications

Technical components in the automotive and electronic industry, where a weight and cost reduction is required

Processing information

The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.


6 Drying time 0 - 4 h

Drying temperature (τ ≤ -30°C) 80°C

Processing moisture 0,02 - 0,1%

1 Feed section 60 - 80°C

2 Temperature zone 1 - Zone 4 220 - 290°C

3 Nozzle temperature 240 - 300°C

4 Melt temperature 240 - 290°C

5 Mold temperature 70 - 100°C

P Nach Holding pressure, spec. 300 - 800 bar

P Stau Back pressure, spec. 50 - 150 bar

Injection speed medium to high

Screw speed 5 - 15 m/min

  • Mechanical Properties
    Tensile modulus (1 mm/min | ISO 527-2)
    d.a.m. 8800 MPa

    Stress at break (5 mm/min | ISO 527-2)
    d.a.m. 135 MPa

    Strain at break (5 mm/min | ISO 527-2)
    d.a.m. 3,1 %

    Charpy notched impact strength (23°C | ISO 179-1/1eA)
    d.a.m. 16 kJ/m²

  • Thermal Properties
    Melting temperature (DSC, 10K/min | DIN EN 11357-1) 220 °C

  • Flammability
    Burning rate (UL 94)
    0,8mm Wall thickness HB Class

    Burning rate (<100 mm/min) (> 1 mm Thickness | FMVSS 302) +

  • General properties
    Density (23°C | ISO 1183) 1,26 g/cm³

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.