PA6 – Polyamide 6 PA6-I GF30

AKROMID® B28 GF 30 S3 white (5242)

9000 MPa

150 MPa

100 kJ/m²

  • 100 kJ/m²

AKROMID® B28 GF 30 S3 white (5242) is a 30% glass fibre reinforced, dry impact resistant, easy flowing polyamide 6 with high stiffness and strength.

Typical applications

Housings and covers for the automotive industry and power tools.

Processing information

The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.
6 Drying time 0 - 4 h
Drying temperature (τ ≤ -30°C) 80°C
Processing moisture 0,02 - 0,1%
1 Feed section 60 - 80°C
2 Temperature zone 1 - Zone 4 240 - 290°C
3 Nozzle temperature 260 - 300°C
4 Melt temperature 270 - 290°C
5 Mold temperature 80 - 100°C
P Nach Holding pressure, spec. 300 - 800 bar
P Stau Back pressure, spec. 50 - 150 bar
Injection speed medium to high
Screw speed 8 - 15 m/min
  • Mechanical Properties
    Tensile modulus (1 mm/min | ISO 527-2)
    d.a.m. 9000 MPa
    Stress at break (5 mm/min | ISO 527-2)
    d.a.m. 150 MPa
    Strain at break (5 mm/min | ISO 527-2)
    d.a.m. 4 %
    Charpy impact strength (23°C | ISO 179-1/1eU)
    d.a.m. 100 kJ/m²
    Charpy notched impact strength (23°C | ISO 179-1/1eA)
    d.a.m. 17 kJ/m²
  • Thermal Properties
    Melting temperature (DSC, 10K/min | DIN EN ISO 11357-3) 220 °C
  • Flammability
    Burning rate (<100 mm/min) (> 1 mm Thickness | FMVSS 302) +
  • General properties
    Molding shrinkage (flow | ISO 294-4) 0,1 - 0,3 %
    Molding shrinkage (transverse | ISO 294-4) 0,5 - 0,7 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.