PA6.6 – Polyamide 6.6 PA66 GF15
AKROMID® A3 GF 15 9 EN natural (5139)
AKROMID® A3 GF 15 9 EN natural (5139) is a 15% fibre reinforced, process improved, electrical neutral polyamide 6.6 with average stiffness and strength.
Components in mechanical engineering and the automotive industry.
Tensile modulus (1 mm/min | ISO 527-2) d.a.m. 5400 MPa
Stress at break (5 mm/min | ISO 527-2) d.a.m. 130 MPa
Strain at break (5 mm/min | ISO 527-2) d.a.m. 3,5 %
Charpy impact strength (23°C | ISO 179-1/1eU) d.a.m. 65 kJ/m²
Charpy notched impact strength (23°C | ISO 179-1/1eA) d.a.m. 7 kJ/m²
Melting temperature (DSC, 10K/min | DIN EN 11357-1) 262 °C
Burning rate (UL 94) 0,8mm Wall thickness HB Class
GWFI (IEC 60695-2-12) 1,6mm Wall thickness 650 °C
Burning rate (<100 mm/min) (> 1 mm Thickness | FMVSS 302) +
Density (23°C | ISO 1183) 1,22 g/cm³
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Ellectrically neutral compound that prevents build up of chrystals on the positive side of a DC system. Suitabel for electric vehicles (EV)
“conditioned” test values = conditioned, measured on test specimens stored according to DIN EN ISO 1110
“d.a.m.” = dry as moulded test values = residual moisture content <0.1%