Preliminary datasheet

PEEK – Polyetheretherketone PEEK GF30

AKROTEK® PEEK GF 30 natural (5047)

12000 MPa

195 MPa

80 kJ/m²

AKROTEK® PEEK GF 30 natural (5047) is a 30% glass fibre reinforced polyetheretherketone with high stiffness and strength.

Typical applications

Elements in the automotive-, aeronautical-, industrial- and medical engineering that require high strength in a temperature environment above 150°C.

Processing information

The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.


6Drying time2 - 3 h

Drying temperature (τ ≤ -30°C)150 - 160°C

Processing moisture< 0,02%

1Feed section60 - 80°C

2Temperature zone 1 - Zone 4365 - 390°C

3Nozzle temperature400°C

4Melting temperature370 - 400°C

5Mold temperature160 - 200°C

P NachHolding pressure, spec.300 - 800 bar

P StauBack pressure, spec.50 bar

Injection speedmedium to high

Screw speed5 - 10 m/min

  • Mechanical Properties
    Tensile modulus (1 mm/min | ISO 527-2)
    d.a.m.12000 MPa
    conditioned12000 MPa

    Stress at break (5 mm/min | ISO 527-2)
    d.a.m.195 MPa
    conditioned185 MPa

    Strain at break (5 mm/min | ISO 527-2)
    d.a.m.2,8 %
    conditioned2,8 %

    Flexural modulus (2 mm/min | ISO 178)
    d.a.m.11500 MPa

    Flexural strength (2 mm/min | ISO 178)
    d.a.m.305 MPa

    Flexural strain at break (2 mm/min | ISO 178)
    d.a.m.3 %

    Charpy impact strength (23°C | ISO 179-1/1eU)
    d.a.m.80 kJ/m²
    conditioned75 kJ/m²

    Charpy notched impact strength (23°C | ISO 179-1/1eA)
    d.a.m.11 kJ/m²
    conditioned11 kJ/m²

  • Thermal Properties
    Temperature of deflection under load HDT/A (1,8 MPa | ISO 75)> 280 °C

    Temperature of deflection under load HDT/C (8 MPa | ISO 75)200 °C

    Melting temperature (DSC, 10K/min | DIN EN 11357-1)342 °C

  • Flammability
    Burning rate (UL 94)
    1,6mm Wall thicknessV0 Class

  • General properties
    Density (23°C | ISO 1183)1,5 g/cm³

    Humidity absorption (70°C, 62% r.F. | ISO 1110)0,1 - 0,2 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.