PA6.6 – Polyamide 6.6 PA66-I GF20 + GB10
AKROMID® A3 GM 20/10 S1 black (4817)
AKROMID® A3 GM 20/10 S1 black (4817) is an 20% glass fibre reinforced, 10% glass bead filled, cold impact strength polyamide 6.6 with good surface and low warpage
Technical devices in automotive and engineering industry capable of carrying high load.
The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.
|Drying time||0 - 4 h|
|Drying temperature (τ ≤ -30°C)||80°C|
|Processing moisture||0,02 - 0,1%|
|Feed section||60 - 80°C|
|Temperature zone 1 - Zone 4||260 - 300°C|
|Nozzle temperature||270 - 310°C|
|Melting temperature||280 - 300°C|
|Mold temperature||80 - 100°C|
|Holding pressure, spec.||300 - 800 bar|
|Back pressure, spec.||50 - 150 bar|
|Injection speed||medium to high|
|Screw speed||8 - 15 m/min|
- Mechanical Properties
Tensile modulus (1 mm/min | ISO 527-2) d.a.m. 6900 MPa conditioned 4200 MPa Stress at break (5 mm/min | ISO 527-2) d.a.m. 130 MPa conditioned 85 MPa Strain at break (5 mm/min | ISO 527-2) d.a.m. 4 % conditioned 10 % Flexural modulus (2 mm/min | ISO 178) d.a.m. 6900 MPa Flexural strength (2 mm/min | ISO 178) d.a.m. 205 MPa Charpy impact strength (23°C | ISO 179-1/1eU) d.a.m. 80 kJ/m² conditioned 80 kJ/m² Charpy impact strength (-30°C | ISO 179-1/1eU) d.a.m. 76 kJ/m² Charpy notched impact strength (23°C | ISO 179-1/1eA) d.a.m. 15 kJ/m² conditioned 16 kJ/m² Charpy notched impact strength (-30°C | ISO 179-1/1eA) d.a.m. 8 kJ/m² Ball indentation hardness (358N/30s | ISO 2039-1) d.a.m. 127 MPa
- Thermal Properties
Temperature of deflection under load HDT/A (1,8 MPa | ISO 75) 245 °C Temperature of deflection under load HDT/B (0,45 MPa | ISO 75) 260 °C Melting temperature (DSC, 10K/min | DIN EN 11357-1) 262 °C
Burning rate UL 94 1,6mm Wall thickness (UL 94) HB Class
- General properties
Density (23°C | ISO 1183) 1,31 g/cm³ Humidity absorption (70°C, 62% r.F. | ISO 1110) 2 % Water absorption 23°C saturated (23°C, saturated | ISO 62) 5,1 % Molding shrinkage (flow | ISO 294-4) 0,5 % Molding shrinkage (transverse | ISO 294-4) 1,3 %
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.