PA6 – Polyamide 6 PA6 GF50

• Mechanical Properties

  Tensile modulus (1 mm/min | ISO 527-2)

  d.a.m.

  16500 MPa

  ---

  Stress at break (5 mm/min | ISO 527-2)

  d.a.m.

  230 MPa

  ---

  Strain at break (5 mm/min | ISO 527-2)

  d.a.m.

  3 %

  ---

  Charpy impact strength (23°C | ISO 179-1/1eU)

  d.a.m.

  105 kJ/m²

  ---

  Charpy notched impact strength (23°C | ISO 179-1/1eA)

  d.a.m.

  20 kJ/m²

  ---

• Thermal Properties

  Melting temperature (DSC, 10K/min | DIN EN ISO 11357-3)

  220 °C

  ---

• Flammability

  Burning rate (UL 94)
  0,8mm Wall thickness	HB Class

  ---

  Burning rate (<100 mm/min) (> 1 mm Thickness | FMVSS 302)

  +

  ---

• General properties

  Density (23°C | ISO 1183)

  1,55 g/cm³

  ---

  Molding shrinkage (flow | ISO 294-4)

  0,1 - 0,3 %

  ---

  Molding shrinkage (transverse | ISO 294-4)

  0,4 - 0,6 %

  ---

Processing information

The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.

	Drying time	0 - 4 h
	Drying temperature (τ ≤ -30°C)	80°C
	Processing moisture	0,02 - 0,1%
	Feed section	60 - 80°C
	Temperature zone 1 - Zone 4	240 - 290°C
	Nozzle temperature	260 - 300°C
	Melt temperature	270 - 290°C
	Mold temperature	80 - 100°C
	Holding pressure, spec.	300 - 800 bar
	Back pressure, spec.	50 - 150 bar
	Injection speed	medium to high
	Screw speed	8 - 15 m/min