Preliminary datasheet

PA6 – Polyamide 6 PA6 + PP GF30

AKROMID® B3 GF 30 1 L natural (4684)

8500 MPa

150 MPa

AKROMID® B3 GF 30 1 L natural (4684) is a 30% glass fibre reinforced and heat stabilised polyamide-blend with a reduced density compared to standard PA6 GF 30

Typical applications

Technical components in the automotive and electronic industry, where a weight and cost reduction is required

Processing information

The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.


6Drying time0 - 4 h

Drying temperature (τ ≤ -30°C)80°C

Processing moisture0,02 - 0,1%

1Feed section60 - 80°C

2Temperature zone 1 - Zone 4220 - 290°C

3Nozzle temperature240 - 300°C

4Melting temperature240 - 290°C

5Mold temperature70 - 100°C

P NachHolding pressure, spec.300 - 800 bar

P StauBack pressure, spec.50 - 150 bar

Injection speedmedium to high

Screw speed5 - 15 m/min

  • Mechanical Properties
    Tensile modulus (1 mm/min | ISO 527-2)
    d.a.m.8500 MPa
    conditioned6500 MPa

    Stress at break (5 mm/min | ISO 527-2)
    d.a.m.150 MPa
    conditioned100 MPa

    Strain at break (5 mm/min | ISO 527-2)
    d.a.m.3,2 %
    conditioned3,7 %

    Flexural modulus (2 mm/min | ISO 178)
    d.a.m.8800 MPa
    conditioned6500 MPa

    Flexural strength (2 mm/min | ISO 178)
    d.a.m.210 MPa
    conditioned150 MPa

    Flexural strain at break (2 mm/min | ISO 178)
    d.a.m.3 %
    conditioned3,9 %

    Charpy impact strength (23°C | ISO 179-1/1eU)
    d.a.m.70 kJ/m²

    Charpy notched impact strength (23°C | ISO 179-1/1eA)
    d.a.m.17 kJ/m²

  • Thermal Properties
    Temperature of deflection under load HDT/A (1,8 MPa | ISO 75)203 °C

    Melting temperature (DSC, 10K/min | DIN EN 11357-1)220 °C

  • Flammability
    Burning rate (UL 94)
    0,8mm Wall thicknessHB Class

    Burning rate (<100 mm/min) (> 1 mm Thickness | FMVSS 302) +

  • General properties
    Density (23°C | ISO 1183)1,26 g/cm³

  • Rheological Properties
    MVR (275°C/5kg | ISO 1133)14 cm³/10min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

You have questions about our products?

With a worldwide network of plastics distribution experts, we can provide you with support anywhere in the world. Talk to one of our specialists to find out more.

CONTACT US NOW