PA6 – Polyamide 6 PA6 + PP GF10 + GB20

AKROMID® B3 GM 10/20 1 L black (4646)

5100 MPa

88 MPa

46 kJ/m²

AKROMID® B3 GM 10/20 1 L black (4646) is a 10% glass fibre reinforced, 20% glass bead filled and heat stabilised polyamide-blend with a reduced density compared to standard PA6 GF10 + GB20

Typical applications

Optical components in the automotive and electronic industry, where a weight and cost reduction is required

Processing information

The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.

6Drying time0 - 4 h
Drying temperature80°C
Processing moisture0,02 - 0,1%
1Feed section60 - 80°C
2Temperature zone 1 - Zone 4220 - 290°C
3Nozzle temperature240 - 300°C
4Melting temperature240 - 290°C
5Mold temperature70 - 100°C
P NachHolding pressure, spec.300 - 800 bar
P StauBack pressure, spec.50 - 150 bar
Injection speedmedium to high
Screw speed5 - 15 m/min
  • Mechanical Properties
    Tensile modulus (1 mm/min | ISO 527-2)
    d.a.m.5100 MPa
    conditioned3300 MPa
    Stress at break (5 mm/min | ISO 527-2)
    d.a.m.88 MPa
    conditioned55 MPa
    Flexural modulus (2 mm/min | ISO 178)
    d.a.m.4700 MPa
    Flexural strength (2 mm/min | ISO 178)
    d.a.m.130 MPa
    Charpy impact strength (23°C | ISO 179-1/1eU)
    d.a.m.46 kJ/m²
    conditioned44 kJ/m²
    Charpy impact strength (-30°C | ISO 179-1/1eU)
    d.a.m.43 kJ/m²
    conditioned42 kJ/m²
    Charpy notched impact strength (23°C | ISO 179-1/1eA)
    d.a.m.7 kJ/m²
    conditioned9 kJ/m²
    Charpy notched impact strength (-30°C | ISO 179-1/1eA)
    d.a.m.4 kJ/m²
    conditioned4 kJ/m²
  • Thermal Properties
    Temperature of deflection under load HDT/A (1,8 MPa | ISO 75)165 °C
    Temperature of deflection under load HDT/B (0,45 MPa | ISO 75)208 °C
    Melting temperature (DSC, 10K/min | DIN EN 11357-1)220 °C
  • Flammability
    Burning rate UL 94 0,8mm Wall thickness (UL 94)HB Class
  • General properties
    Density (23°C | ISO 1183)1,26 g/cm³
    Humidity absorption (70°C, 62% r.F. | ISO 1110)1,4 %
    Molding shrinkage (flow | ISO 294-4)0,5 %
    Molding shrinkage (transverse | ISO 294-4)1,2 %
  • Rheological Properties
    MVR (275°C/5kg | ISO 1133)18 cm³/10min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK® and ICX® are registered trademarks of the Feddersen Group.

You have questions about our products?

With a worldwide network of plastics distribution experts, we can provide you with support anywhere in the world. Talk to one of our specialists to find out more.

CONTACT US NOW