PA6.6/6 – Polyamide 6.6/6 PA66 + PA6 GF 30
AKROMID® C3 GF 30 5 XTC natural (4499)
AKROMID® C3 GF 30 5 XTC natural (4499) is a 30% glass fibre reinforced, high temperature stabilised polaymide 6.6/6 - Blend with high stiffness and strength and extra high temperature tolerance.
Components in mechanical engineering and in the automotive industry.
The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.
|Drying time||0 - 4 h|
|Drying temperature (τ ≤ -30°C)||80°C|
|Processing moisture||0,02 - 0,1%|
|Feed section||60 - 80°C|
|Temperature zone 1 - Zone 4||260 - 300°C|
|Nozzle temperature||270 - 300°C|
|Melt temperature||270 - 300°C|
|Mold temperature||80 - 100°C|
|Holding pressure, spec.||300 - 800 bar|
|Back pressure, spec.||50 - 150 bar|
|Injection speed||medium to high|
|Screw speed||8 - 15 m/min|
Tensile modulus (1 mm/min | ISO 527-2) d.a.m. 9500 MPa conditioned 6000 MPa
Stress at break (5 mm/min | ISO 527-2) d.a.m. 185 MPa conditioned 115 MPa
Strain at break (5 mm/min | ISO 527-2) d.a.m. 3,5 % conditioned 6,5 %
Charpy impact strength (23°C | ISO 179-1/1eU) d.a.m. 95 kJ/m² conditioned 90 kJ/m²
Charpy notched impact strength (23°C | ISO 179-1/1eA) d.a.m. 13 kJ/m² conditioned 13 kJ/m²
Temperature of deflection under load HDT/A (1,8 MPa | ISO 75) 230 °C
Temperature of deflection under load HDT/B (0,45 MPa | ISO 75) 250 °C
Melt temperature (DSC, 10K/min | DIN EN 11357-1) 245 °C
Coefficent of linear thermal expansion, parallel (23°C bis 80°C | ISO 11359-1/2) 0,15 1,0E-4/K
Coefficent of linear thermal expansion, transverse (23°C bis 80°C | ISO 11359-1/2) 1,12 1,0E-4/K
Burning rate (UL 94) 1,6mm Wall thickness HB Class
Burning rate (<100 mm/min) (> 1 mm Thickness | FMVSS 302) +
Density (23°C | ISO 1183) 1,36 g/cm³
Humidity absorption (70°C, 62% r.H. | ISO 1110) 2,0-2,2 %
Molding shrinkage (flow | ISO 294-4) 0,1-0,3 %
Molding shrinkage (transverse | ISO 294-4) 0,4-0,6 %
Volume resistivity (IEC 60093) d.a.m. 1,0E+13 Ohm x cm conditioned 1,0E+10 Ohm x cm
Surface resistivity (acc. to IEC 60093) d.a.m. 1,0E+12 Ohm conditioned 1,0E+10 Ohm
Comparative tracking index (Test liquid A | IEC 60112) 600 V
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.