PA6 – Polyamide 6 PA6 + ABS GF20

• Mechanical Properties

  Tensile modulus (1 mm/min | ISO 527-2)	d.a.m.	6800 MPa
  	conditioned	5000 MPa

  ---

  Stress at break (5 mm/min | ISO 527-2)	d.a.m.	120 MPa
  	conditioned	85 MPa

  ---

  Strain at break (5 mm/min | ISO 527-2)	d.a.m.	2,7 %
  	conditioned	3,5 %

  ---

  Flexural modulus (2 mm/min | ISO 178)

  d.a.m.

  6300 MPa

  ---

  Flexural strength (2 mm/min | ISO 178)

  d.a.m.

  175 MPa

  ---

  Flexural strain at break (2 mm/min | ISO 178)

  d.a.m.

  3,5 %

  ---

  Charpy impact strength (23°C | ISO 179-1/1eU)	d.a.m.	55 kJ/m²
  	conditioned	50 kJ/m²

  ---

  Charpy impact strength (-30°C | ISO 179-1/1eU)	d.a.m.	50 kJ/m²
  	conditioned	50 kJ/m²

  ---

  Charpy notched impact strength (23°C | ISO 179-1/1eA)	d.a.m.	12 kJ/m²
  	conditioned	12 kJ/m²

  ---

  Charpy notched impact strength (-30°C | ISO 179-1/1eA)	d.a.m.	10 kJ/m²
  	conditioned	10 kJ/m²

  ---

  Izod-impact strength (23°C | ISO 180/1U)

  d.a.m.

  50 kJ/m²

  ---

  Izod-notched impact strength (23°C | ISO 180/1A)

  d.a.m.

  12 kJ/m²

  ---

  Ball indentation hardness (961N/30s | ISO 2039-1)

  d.a.m.

  175 MPa

  ---

• Thermal Properties

  Temperature of deflection under load HDT/A (1,8 MPa | ISO 75)

  170 °C

  ---

  Melting temperature (DSC, 10K/min | DIN EN ISO 11357-3)

  220 °C

  ---

• Flammability

  Burning rate (UL 94)
  0,8mm Wall thickness	HB Class

  ---

  Burning rate (<100 mm/min) (> 1 mm Thickness | FMVSS 302)

  +

  ---

• General properties

  Density (23°C | ISO 1183)

  1,24 g/cm³

  ---

  Humidity absorption (70°C, 62% r.H. | ISO 1110)

  1,4 %

  ---

  Molding shrinkage (flow | ISO 294-4)

  0,3 %

  ---

  Molding shrinkage (transverse | ISO 294-4)

  0,55 %

  ---

Processing information

The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.

	Drying time	0 - 4 h
	Drying temperature (τ ≤ -30°C)	80°C
	Processing moisture	0,02 - 0,1%
	Feed section	60 - 80°C
	Temperature zone 1 - Zone 4	220 - 280°C
	Nozzle temperature	240 - 290°C
	Melt temperature	240 - 280°C
	Mold temperature	80 - 100°C
	Holding pressure, spec.	300 - 800 bar
	Back pressure, spec.	50 - 150 bar
	Injection speed	medium to high
	Screw speed	8 - 15 m/min