PA6.6 – Polyamide 6.6 PA66 GB30
AKROMID® A3 GK 30 natural (3689)AKROMID® A3 GK 30 natural (3689) is a PA 6.6 filled with 30% glass beads. It is characterized by a high surface quality and low tendency to warp, which makes it suitable for use in technically demanding components in mechanical engineering and in the automotive industry.
Properties
Tensile Modulus Tensile Strength Impact StrengthFeatures
-
Mechanical Properties
Tensile modulus (1 mm/min | ISO 527-2) d.a.m. 5000 MPa
Stress at break (5 mm/min | ISO 527-2) d.a.m. 90 MPa
Strain at break (5 mm/min | ISO 527-2) d.a.m. 4 %
Flexural modulus (2 mm/min | ISO 178) d.a.m. 4300 MPa
Flexural strength (2 mm/min | ISO 178) d.a.m. 140 MPa
Flexural strain at break (2 mm/min | ISO 178) d.a.m. 6,5 %
Charpy impact strength (23°C | ISO 179-1/1eU) d.a.m. 28 kJ/m²
Charpy impact strength (-30°C | ISO 179-1/1eU) d.a.m. 22 kJ/m²
Charpy notched impact strength (23°C | ISO 179-1/1eA) d.a.m. 4 kJ/m²
Charpy notched impact strength (-30°C | ISO 179-1/1eA) d.a.m. 3 kJ/m²
-
Thermal Properties
Temperature of deflection under load HDT/A (1,8 MPa | ISO 75) 100 °C
Temperature of deflection under load HDT/B (0,45 MPa | ISO 75) 225 °C
Melting temperature (DSC, 10K/min | DIN EN ISO 11357-3) 262 °C
-
Flammability
Burning rate (UL 94) 1,6mm Wall thickness HB Class
GWFI (IEC 60695-2-12) 1,6mm Wall thickness 650 °C
Burning rate (<100 mm/min) (> 1 mm Thickness | FMVSS 302) +
-
General properties
Density (23°C | ISO 1183) 1,35 g/cm³
Humidity absorption (70°C, 62% r.H. | ISO 1110) 2,0 %
Molding shrinkage (flow | ISO 294-4) 1,1 %
Molding shrinkage (transverse | ISO 294-4) 1,3 %
-
Electrical Properties
Surface resistivity (DIN EN 62631-3-2) d.a.m. 1,0E+13 Ω
Comparative tracking index (Test liquid A | IEC 60112) 500 V
-
Sustainability
Recycled content (at least) 30 %
Processing information
The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.
 |
Drying time | 0 - 4 h |
| Drying temperature (τ ≤ -30°C) | 80°C | |
| Processing moisture | 0,02 - 0,1% | |
 |
Feed section | 60 - 80°C |
 |
Temperature zone 1 - Zone 4 | 260 - 300°C |
 |
Nozzle temperature | 270 - 310°C |
 |
Melt temperature | 280 - 300°C |
 |
Mold temperature | 80 - 100°C |
 |
Holding pressure, spec. | 300 - 800 bar |
 |
Back pressure, spec. | 50 - 150 bar |
| Injection speed | medium to high | |
| Screw speed | 8 - 15 m/min | |
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Measuring Curves
Notes
There may be color variations in the natural color, because glass balls are made of glass recyclate.
“d.a.m.” = dry as moulded test values = residual moisture content <0.1%