PA6.10 – Polyamide 6.10 PA610 GF30

AKROMID® S3 GF 30 1 black (3259)

8600 MPa

160 MPa

100 kJ/m²

AKROMID® S3 GF 30 1 black (3259) is a 30% glass fibre reinforced, heat stabilised polyamide 6.10 with high strength and stiffness, lower moisture absorption and high chemical resistance.

Typical applications

Precision parts for apparatus engineering and precision mechanics as well as connectors, housings etc. in the automotive industry.

Processing information

The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.


6Drying time0 - 4 h

Drying temperature (τ ≤ -30°C)80°C

Processing moisture0,02 - 0,1%

1Feed section60 - 80°C

2Temperature zone 1 - Zone 4240 - 290°C

3Nozzle temperature240 - 300°C

4Melting temperature270 - 290°C

5Mold temperature80 - 100°C

P NachHolding pressure, spec.300 - 800 bar

P StauBack pressure, spec.50 - 150 bar

Injection speedmedium to high

Screw speed8 - 15 m/min

  • Mechanical Properties
    Tensile modulus (1 mm/min | ISO 527-2)
    d.a.m.8600 MPa
    conditioned6200 MPa

    Stress at break (5 mm/min | ISO 527-2)
    d.a.m.160 MPa
    conditioned110 MPa

    Strain at break (5 mm/min | ISO 527-2)
    d.a.m.4,5 %
    conditioned7,5 %

    Flexural modulus (2 mm/min | ISO 178)
    d.a.m.7700 MPa

    Flexural strength (2 mm/min | ISO 178)
    d.a.m.230 MPa

    Standard bending strength RP 3,5 (2 mm/min | ISO 178)
    d.a.m.5,5 MPa

    Charpy impact strength (23°C | ISO 179-1/1eU)
    d.a.m.100 kJ/m²
    conditioned100 kJ/m²

    Charpy impact strength (-30°C | ISO 179-1/1eU)
    d.a.m.100 kJ/m²

    Charpy notched impact strength (23°C | ISO 179-1/1eA)
    d.a.m.17 kJ/m²

    Charpy notched impact strength (-30°C | ISO 179-1/1eA)
    d.a.m.12 kJ/m²

    Ball indentation hardness (961N/30s | ISO 2039-1)
    d.a.m.195 MPa

  • Thermal Properties
    Temperature of deflection under load HDT/A (1,8 MPa | ISO 75)205 °C

    Temperature of deflection under load HDT/C (8 MPa | ISO 75)145 °C

    Melting temperature (DSC, 10K/min | DIN EN 11357-1)220 °C

  • Flammability
    Burning rate (UL 94)
    1,6mm Wall thicknessHB Class

    Burning rate (<100 mm/min) (> 1 mm Thickness | FMVSS 302) +

  • General properties
    Density (23°C | ISO 1183)1,31 g/cm³

    Humidity absorption (70°C, 62% r.F. | ISO 1110)1,2 %

    Molding shrinkage (flow | ISO 294-4)0,3 %

    Molding shrinkage (transverse | ISO 294-4)0,9 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.