PA6 – Polyamide 6 PA6 + X GF50

AKROMID® B3 GF 50 4 RM-M black (3221)

AKROMID® B3 GF 50 4 RM-M black (3221) is a 50% glass fiber reinforced polyamide 6, which is distinguished by outstanding surface properties even though its high glass fiber content. Due to its lower moisture uptake, the material is characterised by less mechanical changes in the conditioned state. Furthermore, it is chemically stabilised and therefore perfectly suitable for components in the automotive industry with demands for high resistance against CaCl2 solvents.

Properties

Tensile Modulus
Tensile Strength
Impact Strength

Features

surface modified
reduced moisture
hydrolysis/ chemically stabilised
  • Mechanical Properties

    Tensile modulus (1 mm/min | ISO 527-2) d.a.m. 16500 MPa
    conditioned 13000 MPa

    Stress at break (5 mm/min | ISO 527-2) d.a.m. 210 MPa
    conditioned 160 MPa

    Strain at break (5 mm/min | ISO 527-2) d.a.m. 2 %
    conditioned 2,7 %

    Flexural modulus (2 mm/min | ISO 178) d.a.m. 16800 MPa

    Flexural strength (2 mm/min | ISO 178) d.a.m. 320 MPa

    Charpy impact strength (23°C | ISO 179-1/1eU) d.a.m. 75 kJ/m²
    conditioned 75 kJ/m²

    Charpy impact strength (-30°C | ISO 179-1/1eU) d.a.m. 60 kJ/m²
    conditioned 60 kJ/m²

    Charpy notched impact strength (23°C | ISO 179-1/1eA) d.a.m. 20 kJ/m²
    conditioned 20 kJ/m²

    Charpy notched impact strength (-30°C | ISO 179-1/1eA) d.a.m. 16 kJ/m²
    conditioned 20 kJ/m²

  • Thermal Properties

    Temperature of deflection under load HDT/A (1,8 MPa | ISO 75) 205 °C

    Melting temperature (DSC, 10K/min | DIN EN ISO 11357-3) 225 °C

    Coefficent of linear thermal expansion, parallel (23°C bis 80°C | ISO 11359-1/2) 0,1 1,0E-4/K

    Coefficent of linear thermal expansion, transverse (23°C bis 80°C | ISO 11359-1/2) 0,93 1,0E-4/K

  • Flammability

    Burning rate (UL 94)
    0,8mm Wall thickness HB Class

    Burning rate (<100 mm/min) (> 1 mm Thickness | FMVSS 302) +

  • General properties

    Density (23°C | ISO 1183) 1,6 g/cm³

    Humidity absorption (70°C, 62% r.H. | ISO 1110) 1,1-1,3 %

    Molding shrinkage (flow | ISO 294-4) 0,1 - 0,3 %

    Molding shrinkage (transverse | ISO 294-4) 0,4 - 0,6 %

  • Rheological Properties

    Flowability (2mm Thickness | AKRO) 500 mm

Processing information

The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.


6 Drying time 0 - 4 h

Drying temperature (τ ≤ -30°C) 80°C

Processing moisture 0,02 - 0,1%

1 Feed section 60 - 80°C

2 Temperature zone 1 - Zone 4 220 - 280°C

3 Nozzle temperature 240 - 290°C

4 Melt temperature 240 - 280°C

5 Mold temperature 80 - 100°C

P Nach Holding pressure, spec. 300 - 800 bar

P Stau Back pressure, spec. 50 - 150 bar

Injection speed medium to high

Screw speed 8 - 15 m/min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.