AKROMID® B3 GF 30 RM-M black (3016)

AKROMID® B3 GF 30 RM-M black (3016) is a 30% glass fiber reinforced polyamide 6 with high stiffness and strength. The material is characterised by a lower moisture uptake compared to standard PA 6 GF 30 compounds which results in less mechanical changes in the conditioned state. It is therefore perfectly suitable for components where high dimensional stability is required, e.g. in sports and leisure.

Properties

Tensile Modulus
Tensile Strength
Impact Strength

Features

reduced moisture
sports & leisure
  • Mechanical Properties

    Tensile modulus (1 mm/min | ISO 527-2) d.a.m. 11000 MPa
    conditioned 7100 MPa

    Stress at break (5 mm/min | ISO 527-2) d.a.m. 165 MPa
    conditioned 110 MPa

    Strain at break (5 mm/min | ISO 527-2) d.a.m. 2,6 %
    conditioned 4,5 %

    Flexural modulus (2 mm/min | ISO 178) d.a.m. 9600 MPa

    Flexural strength (2 mm/min | ISO 178) d.a.m. 250 MPa

    Flexural strain at break (2 mm/min | ISO 178) d.a.m. 3,2 %

    Charpy impact strength (23°C | ISO 179-1/1eU) d.a.m. 70 kJ/m²
    conditioned 70 kJ/m²

    Charpy impact strength (-30°C | ISO 179-1/1eU) d.a.m. 65 kJ/m²
    conditioned 60 kJ/m²

    Charpy notched impact strength (23°C | ISO 179-1/1eA) d.a.m. 12 kJ/m²
    conditioned 15 kJ/m²

    Charpy notched impact strength (-30°C | ISO 179-1/1eA) d.a.m. 10 kJ/m²
    conditioned 10 kJ/m²

    Ball indentation hardness (961N/30s | ISO 2039-1) d.a.m. 230 MPa

  • Thermal Properties

    Temperature of deflection under load HDT/A (1,8 MPa | ISO 75) 210 °C

    Melting temperature (DSC, 10K/min | DIN EN ISO 11357-3) 222 °C

  • Flammability

    Burning rate (UL 94)
    0,8mm Wall thickness HB Class
    1,6mm Wall thickness HB Class
    3,2mm Wall thickness HB Class

    Burning rate (<100 mm/min) (> 1 mm Thickness | FMVSS 302) +

  • General properties

    Density (23°C | ISO 1183) 1,41 g/cm³

    Humidity absorption (70°C, 62% r.H. | ISO 1110) 1,5-1,7 %

    Molding shrinkage (flow | ISO 294-4) 0,1-0,3 %

    Molding shrinkage (transverse | ISO 294-4) 0,5-0,7 %

  • Electrical Properties

    Comparative tracking index (Test liquid A | IEC 60112) >600 V

Processing information

The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.


6 Drying time 0 - 4 h

Drying temperature (τ ≤ -30°C) 80°C

Processing moisture 0,02 - 0,1%

1 Feed section 60 - 80°C

2 Temperature zone 1 - Zone 4 220 - 280°C

3 Nozzle temperature 240 - 290°C

4 Melt temperature 240 - 280°C

5 Mold temperature 80 - 100°C

P Nach Holding pressure, spec. 300 - 800 bar

P Stau Back pressure, spec. 50 - 150 bar

Injection speed medium to high

Screw speed 8 - 15 m/min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.