PA6 – Polyamide 6 PA6 GF30
AKROMID® B3 GF 30 1 black (2485)AKROMID® B3 GF 30 1 black (2485) is a 30% glass fiber reinforced polyamide 6. It is characterised by a high stiffness and strength. Furthermore, the material is heat stabilised and therefore perfectly suitable for technical parts in industrial engineering and in the automotive industry.
This grade is also available with biomass balanced PA6: AKROMID® NEXT B3 GF 30 1 black (2485BMB) and with chemically recycled PA6: AKROMID® NEXT B3 GF 30 1 black (2485CMB).
Properties
Tensile Modulus Tensile Strength Impact StrengthFeatures
-
Mechanical Properties
Tensile modulus (1 mm/min | ISO 527-2) d.a.m. 10300 MPa conditioned 6200 MPa
Stress at break (5 mm/min | ISO 527-2) d.a.m. 185 MPa conditioned 110 MPa
Strain at break (5 mm/min | ISO 527-2) d.a.m. 3 % conditioned 5,5 %
Flexural modulus (2 mm/min | ISO 178) d.a.m. 8500 MPa
Flexural strength (2 mm/min | ISO 178) d.a.m. 270 MPa
Charpy impact strength (23°C | ISO 179-1/1eU) d.a.m. 75 kJ/m² conditioned 105 kJ/m²
Charpy impact strength (-30°C | ISO 179-1/1eU) d.a.m. 70 kJ/m² conditioned 85 kJ/m²
Charpy notched impact strength (23°C | ISO 179-1/1eA) d.a.m. 12 kJ/m² conditioned 18 kJ/m²
Charpy notched impact strength (-30°C | ISO 179-1/1eA) d.a.m. 12 kJ/m² conditioned 12 kJ/m²
Ball indentation hardness (961N/30s | ISO 2039-1) d.a.m. 230 MPa
-
Thermal Properties
Temperature of deflection under load HDT/A (1,8 MPa | ISO 75) 210 °C
Temperature of deflection under load HDT/B (0,45 MPa | ISO 75) 220 °C
Temperature of deflection under load HDT/C (8 MPa | ISO 75) 150 °C
Melting temperature (DSC, 10K/min | DIN EN ISO 11357-3) 220 °C
Coefficent of linear thermal expansion, parallel (23°C bis 80°C | ISO 11359-1/2) 0,19 1,0E-4/K
Coefficent of linear thermal expansion, transverse (23°C bis 80°C | ISO 11359-1/2) 1,09 1,0E-4/K
-
Flammability
Burning rate (UL 94) 0,8mm Wall thickness HB Class
GWFI (IEC 60695-2-12) 0,8mm Wall thickness >650 °C 1,6mm Wall thickness >650 °C
Burning rate (<100 mm/min) (> 1 mm Thickness | FMVSS 302) +
-
General properties
Density (23°C | ISO 1183) 1,36 g/cm³
Humidity absorption (70°C, 62% r.H. | ISO 1110) 2,1 - 2,3 %
Water absorption 23°C saturated (23°C, saturated | ISO 62) 6,3 - 6,9 %
Molding shrinkage (flow | ISO 294-4) 0,1 - 0,3 %
Molding shrinkage (transverse | ISO 294-4) 0,5 - 0,7 %
-
Electrical Properties
Volume resistivity (IEC 60093) d.a.m. 1,0E+13 Ω · cm conditioned 1,0E+10 Ω · cm
Volume resistivity (DIN EN 62631-3-1) d.a.m. 1,0E+13 Ω · cm conditioned 1,0E+10 Ω · cm
Surface resistivity (DIN EN 62631-3-2) d.a.m. 1,0E+12 Ω conditioned 1,0E+10 Ω
Comparative tracking index (Test liquid A | IEC 60112) 600 V
Processing information
The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.
 |
Drying time | 0 - 4 h |
| Drying temperature (τ ≤ -30°C) | 80°C | |
| Processing moisture | 0,02 - 0,1% | |
 |
Feed section | 60 - 80°C |
 |
Temperature zone 1 - Zone 4 | 240 - 290°C |
 |
Nozzle temperature | 260 - 300°C |
 |
Melt temperature | 270 - 290°C |
 |
Mold temperature | 80 - 100°C |
 |
Holding pressure, spec. | 300 - 800 bar |
 |
Back pressure, spec. | 50 - 150 bar |
| Injection speed | medium to high | |
| Screw speed | 8 - 15 m/min | |
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Measuring Curves
| – | 260°C |
| – | 280°C |
| – | 300°C |