PA6 – Polyamide 6 PA6-I GF30

AKROMID® B3 GF 30 S1 natural (2165)

9000 MPa

160 MPa

100 kJ/m²

AKROMID® B3 GF 30 S1 natural (2165) is a 30% glass fibre reinforced, cold impact strength polyamide 6 with high stiffness and strength and light inherent color

Typical applications

Housings and covers for the automotive industry and power tools

Processing information

The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.


6 Drying time 0 - 4 h

Drying temperature (τ ≤ -30°C) 80°C

Processing moisture 0,02 - 0,1%

1 Feed section 60 - 80°C

2 Temperature zone 1 - Zone 4 240 - 290°C

3 Nozzle temperature 260 - 300°C

4 Melt temperature 270 - 290°C

5 Mold temperature 80 - 100°C

P Nach Holding pressure, spec. 300 - 800 bar

P Stau Back pressure, spec. 50 - 150 bar

Injection speed medium to high

Screw speed 8 - 15 m/min

  • Mechanical Properties
    Tensile modulus (1 mm/min | ISO 527-2)
    d.a.m. 9000 MPa
    conditioned 5000 MPa

    Stress at break (5 mm/min | ISO 527-2)
    d.a.m. 160 MPa
    conditioned 105 MPa

    Strain at break (5 mm/min | ISO 527-2)
    d.a.m. 5 %
    conditioned 12 %

    Flexural modulus (2 mm/min | ISO 178)
    d.a.m. 8500 MPa
    conditioned 5500 MPa

    Flexural strength (2 mm/min | ISO 178)
    d.a.m. 265 MPa
    conditioned 250 MPa

    Flexural strain at break (2 mm/min | ISO 178)
    d.a.m. 5 %
    conditioned 5,5 %

    Charpy impact strength (23°C | ISO 179-1/1eU)
    d.a.m. 100 kJ/m²

    Charpy impact strength (-30°C | ISO 179-1/1eU)
    d.a.m. 100 kJ/m²
    conditioned n.b. kJ/m²

    Charpy notched impact strength (23°C | ISO 179-1/1eA)
    d.a.m. 25 kJ/m²

    Charpy notched impact strength (-30°C | ISO 179-1/1eA)
    d.a.m. 20 kJ/m²
    conditioned 17 kJ/m²

  • Thermal Properties
    Temperature of deflection under load HDT/A (1,8 MPa | ISO 75) 205 °C

    Temperature of deflection under load HDT/B (0,45 MPa | ISO 75) 220 °C

    Melting temperature (DSC, 10K/min | DIN EN 11357-1) 222 °C

    Temperature index for 50% loss of tensile strength after 20.000h (20.000 Std. | IEC 60216) 115 °C

  • Flammability
    Burning rate (UL 94)
    1,6mm Wall thickness HB Class

    Burning rate (<100 mm/min) (> 1 mm Thickness | FMVSS 302) +

  • General properties
    Density (23°C | ISO 1183) 1,33 g/cm³

    Humidity absorption (70°C, 62% r.H. | ISO 1110) 1,8 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.