PA6 – Polyamide 6 PA6 GB30

AKROMID® B3 GK 30 black (1827)

AKROMID® B3 GK 30 black (1827) is a PA 6 filled with 30% glass beads. It is characterized by a high surface quality and low tendency to warp, which makes it suitable for use in technically demanding components in mechanical engineering and in the automotive industry.

Properties

Tensile Modulus
Tensile Strength
Impact Strength

Features

low warpage
industrial
  • Mechanical Properties

    Tensile modulus (1 mm/min | ISO 527-2) d.a.m. 4500 MPa
    conditioned 2000 MPa

    Stress at break (5 mm/min | ISO 527-2) d.a.m. 75 MPa
    conditioned 40 MPa

    Strain at break (5 mm/min | ISO 527-2) d.a.m. > 3,5 %
    conditioned > 25 %

    Flexural modulus (2 mm/min | ISO 178) d.a.m. 3300 MPa

    Flexural strength (2 mm/min | ISO 178) d.a.m. 110 MPa

    Charpy impact strength (23°C | ISO 179-1/1eU) d.a.m. 20 kJ/m²
    conditioned 40 kJ/m²

    Charpy notched impact strength (23°C | ISO 179-1/1eA) d.a.m. 3 kJ/m²
    conditioned 5 kJ/m²

    Ball indentation hardness (961N/30s | ISO 2039-1) d.a.m. 180 MPa

  • Thermal Properties

    Temperature of deflection under load HDT/A (1,8 MPa | ISO 75) 70 °C

    Temperature of deflection under load HDT/B (0,45 MPa | ISO 75) 185 °C

    Melting temperature (DSC, 10K/min | DIN EN ISO 11357-3) 222 °C

    Temperature index for 50% loss of tensile strength after 5.000h (5.000 h | IEC 60216) 100 °C

    Temperature index for 50% loss of tensile strength after 20.000h (20.000 Std. | IEC 60216) 90 °C

    Vicat softening temperature B50 (50°C/50N | ISO 306) 205 °C

  • Flammability

    Burning rate (UL 94)
    1,6mm Wall thickness HB Class

    GWIT (IEC 60695-2-13)
    1,6mm Wall thickness 675 °C

    Burning rate (<100 mm/min) (> 1 mm Thickness | FMVSS 302) +

  • General properties

    Density (23°C | ISO 1183) 1,34 g/cm³

    Humidity absorption (70°C, 62% r.H. | ISO 1110) 2,0-2,2 %

    Water absorption 23°C saturated (23°C, saturated | ISO 62) 6,5 %

    Molding shrinkage (flow | ISO 294-4) 0,8-1,0 %

    Molding shrinkage (transverse | ISO 294-4) 0,9-1,1 %

  • Rheological Properties

    Flowability (1mm Thickness | AKRO) 120 mm

    Flowability (2mm Thickness | AKRO) 360 mm

  • Sustainability

    Recycled content (at least) 30 %

Processing information

The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.


6 Drying time 0 - 4 h

Drying temperature (τ ≤ -30°C) 80°C

Processing moisture 0,02 - 0,1%

1 Feed section 60 - 80°C

2 Temperature zone 1 - Zone 4 240 - 290°C

3 Nozzle temperature 260 - 300°C

4 Melt temperature 270 - 290°C

5 Mold temperature 80 - 100°C

P Nach Holding pressure, spec. 300 - 800 bar

P Stau Back pressure, spec. 50 - 150 bar

Injection speed medium to high

Screw speed 8 - 15 m/min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.