PA6 – Polyamide 6 PA6-I
AKROMID® B3 3 S3 10 natural (1808)
AKROMID® B3 3 S3 10 natural (1808) is an unreinforced, nucleated, dry impact resistant polyamide 6 with light inherent color.
Handles and fittings for power tools and furniture industry.
The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.
|Drying time||0 - 4 h|
|Drying temperature (τ ≤ -30°C)||80°C|
|Processing moisture||0,02 - 0,1%|
|Feed section||60 - 80°C|
|Temperature zone 1 - Zone 4||220 - 270°C|
|Nozzle temperature||230 - 300°C|
|Melting temperature||240 - 270°C|
|Mold temperature||40 - 80°C|
|Holding pressure, spec.||300 - 800 bar|
|Back pressure, spec.||50 - 150 bar|
|Injection speed||medium to high|
|Screw speed||8 - 15 m/min|
- Mechanical Properties
Tensile modulus (1 mm/min | ISO 527-2) d.a.m. 2700 MPa conditioned 955 MPa Stress at yield (50 mm/min | ISO 527-2) d.a.m. 70 MPa conditioned 40 MPa Strain at yield (50 mm/min | ISO 527-2) d.a.m. 4,3 % conditioned 15 % Strain at break (50 mm/min | ISO 527-2) d.a.m. > 45 % conditioned > 100 % Flexural modulus (2 mm/min | ISO 178) d.a.m. 2600 MPa conditioned 950 MPa Charpy impact strength (23°C | ISO 179-1/1eU) d.a.m. n.b. conditioned n.b. Charpy impact strength (-30°C | ISO 179-1/1eU) d.a.m. n.b. conditioned n.b. Charpy notched impact strength (23°C | ISO 179-1/1eA) d.a.m. 10 kJ/m² conditioned 28 kJ/m² Charpy notched impact strength (-30°C | ISO 179-1/1eA) d.a.m. 8 kJ/m² conditioned 10 kJ/m² Ball indentation hardness (358N/30s | ISO 2039-1) d.a.m. 102 MPa
- Thermal Properties
Temperature of deflection under load HDT/A (1,8 MPa | ISO 75) 60 °C Temperature of deflection under load HDT/B (0,45 MPa | ISO 75) 162 °C Melting temperature (DSC, 10K/min | DIN EN 11357-1) 222 °C
Burning rate (UL 94) 1,6mm Wall thickness HB Class Burning rate (<100 mm/min) (> 1 mm Thickness | FMVSS 302) +
- General properties
Density (23°C | ISO 1183) 1,1 g/cm³ Humidity absorption (70°C, 62% r.F. | ISO 1110) 2,6 % Molding shrinkage (flow | ISO 294-4) 1,0 - 1,2 % Molding shrinkage (transverse | ISO 294-4) 1,1 - 1,3 %
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
You have questions about our products?
With a worldwide network of plastics distribution experts, we can provide you with support anywhere in the world. Talk to one of our specialists to find out more.CONTACT US NOW