PA6.6 – Polyamide 6.6 PA66-I
AKROMID® A3 5 S3 15 black (1434)
AKROMID® A3 5 S3 15 black 950058 (1434) is a nonreinforced, high temperature stabilised, dry impact resistant polyamide 6.6.
Connecting and fixing systems, used at elevated temperatures in the automotive and electro industry
The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.
|Drying time||0 - 4 h|
|Drying temperature (τ ≤ -30°C)||80°C|
|Processing moisture||0,02 - 0,1%|
|Feed section||60 - 80°C|
|Temperature zone 1 - Zone 4||260 - 300°C|
|Nozzle temperature||270 - 310°C|
|Melting temperature||280 - 300°C|
|Mold temperature||40 - 80°C|
|Holding pressure, spec.||300 - 800 bar|
|Back pressure, spec.||50 - 150 bar|
|Injection speed||medium to high|
|Screw speed||8 - 15 m/min|
- Mechanical Properties
Tensile modulus (1 mm/min | ISO 527-2) d.a.m. 2500 MPa conditioned 1200 MPa Stress at yield (50 mm/min | ISO 527-2) d.a.m. 65 MPa conditioned 45 MPa Strain at yield (50 mm/min | ISO 527-2) d.a.m. 7 % conditioned 24 % Strain at break (50 mm/min | ISO 527-2) d.a.m. 30 % conditioned > 100 % Flexural modulus (2 mm/min | ISO 178) d.a.m. 2500 MPa Flexural strength (2 mm/min | ISO 178) d.a.m. 95 MPa Flexural strain at break (2 mm/min | ISO 178) d.a.m. 7,5 % Charpy impact strength (23°C | ISO 179-1/1eU) d.a.m. n.b. kJ/m² conditioned n.b. kJ/m² Charpy impact strength (-30°C | ISO 179-1/1eU) d.a.m. o.B. kJ/m² conditioned o.B. kJ/m² Charpy notched impact strength (23°C | ISO 179-1/1eA) d.a.m. 15 kJ/m² Charpy notched impact strength (-30°C | ISO 179-1/1eA) d.a.m. 13 kJ/m²
- Thermal Properties
Melting temperature (DSC, 10K/min | DIN EN 11357-1) 262 °C
Burning rate (UL 94) 1,6mm Wall thickness HB Class Burning rate (<100 mm/min) (> 1 mm Thickness | FMVSS 302) +
- General properties
Density (23°C | ISO 1183) 1,11 g/cm³ Humidity absorption (70°C, 62% r.F. | ISO 1110) 1,9 %
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.