PA6 – Polyamide 6 PA6-I GF30

• Mechanical Properties

  Tensile modulus (1 mm/min | ISO 527-2)	d.a.m.	8800 MPa
  	conditioned	5500 MPa

  ---

  Stress at break (5 mm/min | ISO 527-2)	d.a.m.	150 MPa
  	conditioned	90 MPa

  ---

  Strain at break (5 mm/min | ISO 527-2)	d.a.m.	3,5 %
  	conditioned	6 %

  ---

  Flexural modulus (2 mm/min | ISO 178)

  d.a.m.

  8300 MPa

  ---

  Charpy impact strength (23°C | ISO 179-1/1eU)	d.a.m.	85 kJ/m²
  	conditioned	100 kJ/m²

  ---

  Charpy notched impact strength (23°C | ISO 179-1/1eA)	d.a.m.	15 kJ/m²
  	conditioned	20 kJ/m²

  ---

  Charpy notched impact strength (-30°C | ISO 179-1/1eA)

  d.a.m.

  10 kJ/m²

  ---

• Thermal Properties

  Temperature of deflection under load HDT/A (1,8 MPa | ISO 75)

  190 °C

  ---

  Melting temperature (DSC, 10K/min | DIN EN ISO 11357-3)

  222 °C

  ---

• Flammability

  Burning rate (UL 94)
  1,6mm Wall thickness	HB Class

  ---

  Burning rate (<100 mm/min) (> 1 mm Thickness | FMVSS 302)

  +

  ---

• General properties

  Density (23°C | ISO 1183)

  1,35 g/cm³

  ---

  Molding shrinkage (flow | ISO 294-4)

  0,1 - 0,3 %

  ---

  Molding shrinkage (transverse | ISO 294-4)

  0,5 - 0,7 %

  ---

• Rheological Properties

  MVR (275°C/5kg | ISO 1133)

  25 cm³/10min

  ---

Processing information

The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.

	Drying time	0 - 4 h
	Drying temperature (τ ≤ -30°C)	80°C
	Processing moisture	0,02 - 0,1%
	Feed section	60 - 80°C
	Temperature zone 1 - Zone 4	240 - 290°C
	Nozzle temperature	260 - 300°C
	Melt temperature	270 - 290°C
	Mold temperature	80 - 100°C
	Holding pressure, spec.	300 - 800 bar
	Back pressure, spec.	50 - 150 bar
	Injection speed	medium to high
	Screw speed	8 - 15 m/min