PA6.6 – Polyamide 6.6 PA66 GF15 + GB15

AKROMID® A3 GM 15/15 black (1073)

7600 MPa

145 MPa

41 kJ/m²

AKROMID® A3 GM 15/15 black (1073) is a 15% glass fibre reinforced, 15% glass bead filled polyamide 6.6 with good surface and low warpage.

Typical applications

Components in mechanical enginneering and automotive industry with high surface requirements

Processing information

The listed values are recommendations. Higher values should be used for higher glass loadings. We recommend only de-humidifying or vacuum dryers. Extensive drying can cause filling problems and surface defects.


6 Drying time 0 - 4 h

Drying temperature (τ ≤ -30°C) 80°C

Processing moisture 0,02 - 0,1%

1 Feed section 60 - 80°C

2 Temperature zone 1 - Zone 4 260 - 300°C

3 Nozzle temperature 270 - 310°C

4 Melt temperature 280 - 300°C

5 Mold temperature 80 - 100°C

P Nach Holding pressure, spec. 300 - 800 bar

P Stau Back pressure, spec. 50 - 150 bar

Injection speed medium to high

Screw speed 8 - 15 m/min

  • Mechanical Properties
    Tensile modulus (1 mm/min | ISO 527-2)
    d.a.m. 7600 MPa
    conditioned 4600 MPa

    Stress at break (5 mm/min | ISO 527-2)
    d.a.m. 145 MPa
    conditioned 90 MPa

    Strain at break (5 mm/min | ISO 527-2)
    d.a.m. 3 %
    conditioned 8 %

    Flexural modulus (2 mm/min | ISO 178)
    d.a.m. 7500 MPa
    conditioned 6200 MPa

    Flexural strength (2 mm/min | ISO 178)
    d.a.m. 220 MPa
    conditioned 155 MPa

    Charpy impact strength (23°C | ISO 179-1/1eU)
    d.a.m. 41 kJ/m²
    conditioned 75 kJ/m²

    Charpy notched impact strength (23°C | ISO 179-1/1eA)
    d.a.m. 6 kJ/m²
    conditioned 7 kJ/m²

  • Thermal Properties
    Temperature of deflection under load HDT/A (1,8 MPa | ISO 75) 244 °C

    Temperature of deflection under load HDT/B (0,45 MPa | ISO 75) 263 °C

    Melting temperature (DSC, 10K/min | DIN EN 11357-1) 262 °C

  • Flammability
    Burning rate (UL 94)
    1,6mm Wall thickness HB Class

    Burning rate (<100 mm/min) (> 1 mm Thickness | FMVSS 302) +

  • General properties
    Density (23°C | ISO 1183) 1,35 g/cm³

    Humidity absorption (70°C, 62% r.H. | ISO 1110) 1,4 %

    Water absorption 23°C saturated (23°C, saturated | ISO 62) 5,6 %

    Molding shrinkage (flow | ISO 294-4) 0,4 %

    Molding shrinkage (transverse | ISO 294-4) 1,4 %

  • Electrical Properties
    Volume resistivity (IEC 60093)
    d.a.m. 1,0E+15 Ohm x cm

    Surface resistivity (acc. to IEC 60093)
    d.a.m. 1,0E+13 Ohm

    Comparative tracking index (Test liquid A | IEC 60112) 500 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.